Method of fabricating cigs by selenization at high temperature

ABSTRACT

A method for high temperature selenization of Cu—In—Ga metal precursor films comprises a partial selenization at a temperature between about 350 C and about 450 C in a Se-containing atmosphere followed by a more fully selenization step at a temperature between about 550 C and about 650 C in a Se-containing atmosphere. The Se-containing component of the atmosphere is removed through a rapid gas exchange process and the CIGS film is annealed to influence the Ga distribution throughout the depth of the film.

FIELD OF THE INVENTION

The present invention relates generally to methods for selenizing thin film solar cells at high temperatures. More specifically, methods of selenizing copper indium gallium (sulfide) selenide (CIG(S)Se, or CIGS) solar cells.

BACKGROUND OF THE INVENTION

Solar cells are photovoltaic (PV) devices that convert light into electrical energy. Solar cells have been developed as clean, renewable energy sources to meet growing demand. Solar cells have been implemented in a wide number of commercial markets including residential rooftops, commercial rooftops, utility-scale PV projects, building integrated PV (BIPV), building applied PV (BAPV), PV in electronic devices, PV in clothing, etc. Currently, crystalline silicon solar cells (both single crystal and polycrystalline) are the dominant technologies in the market. Crystalline silicon (cSi) solar cells must use a thick substrate (>100 um) of silicon to absorb the sunlight since it has an indirect band gap. Also, the absorption coefficient is low for crystalline silicon because of the indirect band gap. The use of a thick substrate also means that the crystalline silicon solar cells must use high quality material to provide long minority carrier lifetimes to allow the carriers to diffuse to the p-n junction. Therefore, crystalline silicon solar cell technologies lead to increased costs. Thin film photovoltaic (TFPV) solar devices based on amorphous silicon (a-Si), CIGS, CdTe, CZTS, etc. provide an opportunity to increase the material utilization since only thin films (<10 um) are generally required. The thin film solar cells may be formed from amorphous, nanocrystalline, micro-crystalline, or mono-crystalline materials. TFPV devices may have a single device configuration (i.e. they are comprised of a single light conversion device) or they may have a tandem configuration wherein multiple TFPV devices are used to increase the absorption efficiency within different wavelength regions of the incident light spectrum.

TFPV devices provide an opportunity to reduce energy payback time, and reduce water usage for solar panel manufacturing. The absorption coefficient for CIGS is about 10⁵/cm. CIGS films have bandgaps in the range of 1.0 eV (CIS) to 1.65 eV (CGS) and are also efficient absorbers across the entire visible spectrum. Among the thin film solar technologies, CIGS has demonstrated the best lab cell efficiency (over 20%) and the best large area module efficiency (>15%).

A general class of PV absorber films of special interest is formed as multinary compounds from Groups IB-IIIA-VIA of the periodic table. Group IB includes Cu, Ag, and Au. Group IIA includes B, Al, Ga, In, and TI. Group VIA includes O, S, Se, Te, and Po. Additionally, the IB-IIIA-VIA materials can be doped with dopants from Groups VIII, IIB, IVA, VA, and VIIA of the periodic table. Group VII includes Fe, Ru, Os, Co, Rh, Ir, Ni, Pd, and Pt. Group IIB includes Zn, Cd, and Hg. Group IVA includes C, Si, Ge, Sn, and Pb. Group VA includes N, P, As, Sb, and Bi. Group VIIA includes F, CI, Br, I, and At. Other potential absorber materials of interest include cuprous oxide, iron sulfide, etc.

TFPV devices can be fabricated at the cell level or the panel level, thus further decreasing the manufacturing costs. As used herein, the cell level is understood to mean an individual unit that can be combined with other units to form a module. The cells may be rigid or flexible. As used herein, the panel level is understood to mean a large TFPV structure that is not composed of smaller units. Generally, the panels are similar in size to the aforementioned modules. For economy of language, the phrase “TFPV device” will be understood to refer to either a solar cell or a panel without distinction. Furthermore, TFPV devices may be fabricated on inexpensive substrates such as glass, plastics, and thin sheets of metal. Examples of suitable substrates comprise float glass, low-iron glass, borosilicate glass, flexible glass, specialty glass for high temperature processing, stainless steel, carbon steel, aluminum, copper, polyimide, plastics, etc. Furthermore, the substrates may be processed in many configurations such as single substrate processing, multiple substrate batch processing, inline continuous processing, roll-to-roll processing, etc.

The increasing demand for environmentally friendly, sustainable and renewable energy sources is driving the development of large area, thin film photovoltaic devices. With a long-term goal of providing a significant percentage of global energy demand, there is a concomitant need for Earth-abundant, high conversion efficiency materials for use in photovoltaic devices. A number of Earth abundant direct-bandgap semiconductor materials now seem to show evidence of the potential for both high efficiency and low cost in Very Large Scale (VLS) production (e.g. greater than 100 gigawatt (GW)), yet their development and characterization remains difficult because of the complexity of the materials systems involved.

The immaturity of TFPV devices exploiting Earth abundant materials represents a daunting challenge in terms of the time-to-commercialization. That same immaturity also suggests an enticing opportunity for breakthrough discoveries. A quaternary system such as CIGS requires management of multiple kinetic pathways, thermodynamic phase equilibrium considerations, defect chemistries, and interfacial control. The vast phase-space to be managed includes process parameters, source material choices, compositions, and overall integration schemes. The complexity of the intrinsically-doped, self-compensating, multinary, polycrystalline, queue-time-sensitive, thin-film absorber (CIGS), and its interfaces to up-, and down-stream processing, combined with the lack of knowledge on a device level to address efficiency losses effectively, makes it a highly empirical material system. The performance of any thin-film, (opto-)electronically-active device is extremely sensitive to its interfaces. Interface engineering for electronically-active devices is highly empirical. Traditional R&D methods are ill-equipped to address such complexity, and the traditionally slow pace of R&D could limit any new material from reaching industrial relevance when having to compete with the incrementally improving performance of already established TFPV fabrication lines, and continuously decreasing panel prices for more traditional cSi PV technologies.

However, due to the complexity of the material, cell structure and manufacturing process, both the fundamental scientific understanding and large scale manufacturability are yet to be improved for CIGS TFPV devices. As the photovoltaic industry pushes to achieve grid parity, much faster and broader investigation is needed to explore the material, device, and process windows for higher efficiency and a lower cost of manufacturing process. Efficient methods for forming different types of CIGS TFPV devices that can be evaluated are necessary.

Typically, CIGS is formed by the selenization of Cu—In—Ga precursors that have been previously deposited. The selenization is typically performed in a batch furnace using H₂Se gas as the source of Se. A common problem encountered in this process is the Ga segregation towards the Mo back contact due to the different reaction kinetics of In and Ga with H₂Se. This produces a non-uniform band gap in the depth of the absorber. The Ga poor surface layer has low band gap that limits the V_(oc) of the solar cell. In addition, the lattice mismatch caused by the large inhomogeneity in depth can introduce structural defects and recombination centers in the space charge region, which adversely impacts device performance. For large area CIGS thin film modules, high V_(oc) is important for performance improvement because series resistance losses need to be minimized. A reasonable criteria for high efficiency modules is V_(oc) greater than 600 mV. Another benefit of high band gap solar cells is better performance in hot climates due to better temperature coefficients. Therefore, there is a need to develop systems and methods for the selenization of Cu—In—Ga films that allow the production of high performance CIGS films with control over the Ga distribution.

SUMMARY OF THE DISCLOSURE

In some embodiments of the present invention, a high temperature process is used for the selenization of Cu—In—Ga films. In a first step, a low temperature (<about 450 C) partial selenization step is used to react the Se with In in the precursor film. This step prevents In agglomeration during subsequent higher temperature steps and results in smoother films. The next step is a high temperature selenization step at about 625 C for between about 1 minute and about 10 minutes. This step is followed by a fast gas exchange to replace the H₂Se gas with an inert gas to stop the selenization step. Finally, a high temperature (about 625 C) anneal in an inert gas is used to enhance Ga diffusion and tune the gradient of the band gap.

BRIEF DESCRIPTION OF THE DRAWINGS

To facilitate understanding, identical reference numerals have been used, where possible, to designate identical elements that are common to the figures. The drawings are not to scale and the relative dimensions of various elements in the drawings are depicted schematically and not necessarily to scale.

The techniques of the present invention can readily be understood by considering the following detailed description in conjunction with the accompanying drawings, in which:

FIG. 1 is a schematic diagram for implementing combinatorial processing and evaluation.

FIG. 2 is a schematic diagram for illustrating various process sequences using combinatorial processing and evaluation.

FIG. 3 illustrates a schematic diagram of a simple substrate TFPV stack according to an embodiment described herein.

FIG. 4 illustrates a schematic diagram of a combinatorial PVD system according to an embodiment described herein.

FIG. 5 illustrates a schematic diagram of a substrate that has been processed in a combinatorial manner.

FIG. 6 presents SEM micrographs of CIG films formed using different sequences.

FIG. 7 illustrates a schematic diagram of furnace temperature profiles for the standard 500 C process and the 625 C process described in some embodiments herein.

FIG. 8 presents SEM micrographs of CIGS films formed using different selenization treatments.

FIG. 9 presents photoluminescence data from CIGS films formed using different selenization treatments.

FIG. 10 illustrates a flow chart that summarizes the salient steps of the methods used in some embodiments of the present invention.

DETAILED DESCRIPTION

A detailed description of one or more embodiments is provided below along with accompanying figures. The detailed description is provided in connection with such embodiments, but is not limited to any particular example. The scope is limited only by the claims and numerous alternatives, modifications, and equivalents are encompassed. Numerous specific details are set forth in the following description in order to provide a thorough understanding. These details are provided for the purpose of example and the described techniques may be practiced according to the claims without some or all of these specific details. For the purpose of clarity, technical material that is known in the technical fields related to the embodiments has not been described in detail to avoid unnecessarily obscuring the description.

As used herein, “CIGS” will be understood to represent the entire range of related alloys denoted by Cu_(z)In_((1−x))Ga_(x)S_((2+w)(1−y))Se_((2+w)y), where 0.5≦z≦1.5, 0≦x≦1, 0≦y≦1, −0.2≦w≦0.5 As used herein, “CZTS” will be understood to represent the entire range of related alloys denoted by Cu₂ZnSn(S_(y)Se_(1−y))₄ where 0≦y≦1. Similarly, as noted above, other IB-IIIA-VIA materials may be used as potential absorber layers. Also as mentioned previously, any of these materials may be further doped with a suitable dopant.

In FIG. 3 below, a TFPV material stack is illustrated using a simple planar structure. Those skilled in the art will appreciate that the description and teachings to follow can be readily applied to any simple or complex TFPV solar cell morphology. The drawings are for illustrative purposes only and do not limit the application of the present invention.

The efficiency of TFPV devices depends on many properties of the absorber layer such as crystallinity, grain size, composition uniformity, density, defect concentration, doping level, surface roughness, etc. These properties may be influenced by the details of the process conditions under which the layer is formed or treated.

The manufacture of TFPV devices entails the integration and sequencing of many unit processing steps. As an example, TFPV manufacturing typically includes a series of processing steps such as cleaning, surface preparation, deposition, patterning, etching, thermal annealing, and other related unit processing steps. The precise sequencing and integration of the unit processing steps enables the formation of functional devices meeting desired performance metrics such as efficiency, power production, and reliability.

As part of the discovery, optimization and qualification of each unit process, it is desirable to be able to i) test different materials, ii) test different processing conditions within each unit process module, iii) test different sequencing and integration of processing modules within an integrated processing tool, iv) test different sequencing of processing tools in executing different process sequence integration flows, and combinations thereof in the manufacture of devices such as TFPV devices. In particular, there is a need to be able to test i) more than one material, ii) more than one processing condition, iii) more than one sequence of processing conditions, iv) more than one process sequence integration flow, and combinations thereof, collectively known as “combinatorial process sequence integration”, on a single substrate without the need of consuming the equivalent number of monolithic substrates per material(s), processing condition(s), sequence(s) of processing conditions, sequence(s) of processes, and combinations thereof. This can greatly improve both the speed and reduce the costs associated with the discovery, implementation, optimization, and qualification of material(s), process(es), and process integration sequence(s) required for manufacturing.

Systems and methods for High Productivity Combinatorial (HPC) processing are described in U.S. Pat. No. 7,544,574 filed on Feb. 10, 2006, U.S. Pat. No. 7,824,935 filed on Jul. 2, 2008, U.S. Pat. No. 7,871,928 filed on May 4, 2009, U.S. Pat. No. 7,902,063 filed on Feb. 10, 2006, and U.S. Pat. No. 7,947,531 filed on Aug. 28, 2009 which are all herein incorporated by reference. Systems and methods for HPC processing are further described in U.S. patent application Ser. No. 11/352,077 filed on Feb. 10, 2006, claiming priority from Oct. 15, 2005, U.S. patent application Ser. No. 11/419,174 filed on May 18, 2006, claiming priority from Oct. 15, 2005, U.S. patent application Ser. No. 11/674,132 filed on Feb. 12, 2007, claiming priority from Oct. 15, 2005, and U.S. patent application Ser. No. 11/674,137 filed on Feb. 12, 2007, claiming priority from Oct. 15, 2005 which are all herein incorporated by reference.

HPC processing techniques have been successfully adapted to wet chemical processing such as etching, texturing, polishing, cleaning, etc. HPC processing techniques have also been successfully adapted to deposition processes such as sputtering, atomic layer deposition (ALD), and chemical vapor deposition (CVD).

FIG. 1 illustrates a schematic diagram, 100, for implementing combinatorial processing and evaluation using primary, secondary, and tertiary screening. The schematic diagram, 100, illustrates that the relative number of combinatorial processes run with a group of substrates decreases as certain materials and/or processes are selected. Generally, combinatorial processing includes performing a large number of processes during a primary screen, selecting promising candidates from those processes, performing the selected processing during a secondary screen, selecting promising candidates from the secondary screen for a tertiary screen, and so on. In addition, feedback from later stages to earlier stages can be used to refine the success criteria and provide better screening results.

For example, thousands of materials are evaluated during a materials discovery stage, 102. Materials discovery stage, 102, is also known as a primary screening stage performed using primary screening techniques. Primary screening techniques may include dividing substrates into coupons and depositing materials using varied processes. The materials are then evaluated, and promising candidates are advanced to the secondary screen, or materials and process development stage, 104. Evaluation of the materials is performed using metrology tools such as electronic testers and imaging tools (i.e., microscopes).

The materials and process development stage, 104, may evaluate hundreds of materials (i.e., a magnitude smaller than the primary stage) and may focus on the processes used to deposit or develop those materials. Promising materials and processes are again selected, and advanced to the tertiary screen or process integration stage, 106, where tens of materials and/or processes and combinations are evaluated. The tertiary screen or process integration stage, 106, may focus on integrating the selected processes and materials with other processes and materials.

The most promising materials and processes from the tertiary screen are advanced to device qualification, 108. In device qualification, the materials and processes selected are evaluated for high volume manufacturing, which normally is conducted on full substrates within production tools, but need not be conducted in such a manner. The results are evaluated to determine the efficacy of the selected materials and processes. If successful, the use of the screened materials and processes can proceed to pilot manufacturing, 110.

The schematic diagram, 100, is an example of various techniques that may be used to evaluate and select materials and processes for the development of new materials and processes. The descriptions of primary, secondary, etc. screening and the various stages, 102-110, are arbitrary and the stages may overlap, occur out of sequence, be described and be performed in many other ways.

This application benefits from High Productivity Combinatorial (HPC) techniques described in U.S. patent application Ser. No. 11/674,137 filed on Feb. 12, 2007 which is hereby incorporated for reference in its entirety. Portions of the '137 application have been reproduced below to enhance the understanding of the present invention. The embodiments described herein enable the application of combinatorial techniques to process sequence integration in order to arrive at a globally optimal sequence of TFPV manufacturing operations by considering interaction effects between the unit manufacturing operations, the process conditions used to effect such unit manufacturing operations, hardware details used during the processing, as well as materials characteristics of components utilized within the unit manufacturing operations. Rather than only considering a series of local optimums, i.e., where the best conditions and materials for each manufacturing unit operation is considered in isolation, the embodiments described below consider interactions effects introduced due to the multitude of processing operations that are performed and the order in which such multitude of processing operations are performed when fabricating a TFPV device. A global optimum sequence order is therefore derived and as part of this derivation, the unit processes, unit process parameters and materials used in the unit process operations of the optimum sequence order are also considered.

The embodiments described further analyze a portion or sub-set of the overall process sequence used to manufacture a TFPV device. Once the subset of the process sequence is identified for analysis, combinatorial process sequence integration testing is performed to optimize the materials, unit processes, hardware details, and process sequence used to build that portion of the device or structure. During the processing of some embodiments described herein, structures are formed on the processed substrate that are equivalent to the structures formed during actual production of the TFPV device. For example, such structures may include, but would not be limited to, contact layers, buffer layers, absorber layers, or any other series of layers or unit processes that create an intermediate structure found on TFPV devices. While the combinatorial processing varies certain materials, unit processes, hardware details, or process sequences, the composition or thickness of the layers or structures or the action of the unit process, such as cleaning, surface preparation, deposition, surface treatment, etc. is substantially uniform through each discrete region. Furthermore, while different materials or unit processes may be used for corresponding layers or steps in the formation of a structure in different regions of the substrate during the combinatorial processing, the application of each layer or use of a given unit process is substantially consistent or uniform throughout the different regions in which it is intentionally applied. Thus, the processing is uniform within a region (inter-region uniformity) and between regions (intra-region uniformity), as desired. It should be noted that the process can be varied between regions, for example, where a thickness of a layer is varied or a material may be varied between the regions, etc., as desired by the design of the experiment.

The result is a series of regions on the substrate that contain structures or unit process sequences that have been uniformly applied within that region and, as applicable, across different regions. This process uniformity allows comparison of the properties within and across the different regions such that the variations in test results are due to the varied parameter (e.g., materials, unit processes, unit process parameters, hardware details, or process sequences) and not the lack of process uniformity. In the embodiments described herein, the positions of the discrete regions on the substrate can be defined as needed, but are preferably systematized for ease of tooling and design of experimentation. In addition, the number, variants and location of structures within each region are designed to enable valid statistical analysis of the test results within each region and across regions to be performed.

FIG. 2 is a simplified schematic diagram illustrating a general methodology for combinatorial process sequence integration that includes site isolated processing and/or conventional processing in accordance with one embodiment of the invention. In one embodiment, the substrate is initially processed using conventional process N. In one exemplary embodiment, the substrate is then processed using site isolated process N+1. During site isolated processing, an HPC module may be used, such as the HPC module described in U.S. patent application Ser. No. 11/352,077 filed on Feb. 10, 2006. The substrate can then be processed using site isolated process N+2, and thereafter processed using conventional process N+3. Testing is performed and the results are evaluated. The testing can include physical, chemical, acoustic, magnetic, electrical, optical, etc. tests. From this evaluation, a particular process from the various site isolated processes (e.g. from steps N+1 and N+2) may be selected and fixed so that additional combinatorial process sequence integration may be performed using site isolated processing for either process N or N+3. For example, a next process sequence can include processing the substrate using site isolated process N, conventional processing for processes N+1, N+2, and N+3, with testing performed thereafter.

It should be appreciated that various other combinations of conventional and combinatorial processes can be included in the processing sequence with regard to FIG. 2. That is, the combinatorial process sequence integration can be applied to any desired segments and/or portions of an overall process flow. Characterization, including physical, chemical, acoustic, magnetic, electrical, optical, etc. testing, can be performed after each process operation, and/or series of process operations within the process flow as desired. The feedback provided by the testing is used to select certain materials, processes, process conditions, and process sequences and eliminate others. Furthermore, the above flows can be applied to entire monolithic substrates, or portions of monolithic substrates such as coupons.

Under combinatorial processing operations the processing conditions at different regions can be controlled independently. Consequently, process material amounts, reactant species, processing temperatures, processing times, processing pressures, processing flow rates, processing powers, processing reagent compositions, the rates at which the reactions are quenched, deposition order of process materials, process sequence steps, hardware details, etc., can be varied from region to region on the substrate. Thus, for example, when exploring materials, a processing material delivered to a first and second region can be the same or different. If the processing material delivered to the first region is the same as the processing material delivered to the second region, this processing material can be offered to the first and second regions on the substrate at different concentrations. In addition, the material can be deposited under different processing parameters. Parameters which can be varied include, but are not limited to, process material amounts, reactant species, processing temperatures, processing times, processing pressures, processing flow rates, processing powers, processing reagent compositions, the rates at which the reactions are quenched, atmospheres in which the processes are conducted, an order in which materials are deposited, hardware details of the gas distribution assembly, etc. It should be appreciated that these process parameters are exemplary and not meant to be an exhaustive list as other process parameters commonly used in TFPV manufacturing may be varied.

As mentioned above, within a region, the process conditions are substantially uniform, in contrast to gradient processing techniques which rely on the inherent non-uniformity of the material deposition. That is, the embodiments, described herein locally perform the processing in a conventional manner, e.g., substantially consistent and substantially uniform, while globally over the substrate, the materials, processes, and process sequences may vary. Thus, the testing will find optimums without interference from process variation differences between processes that are meant to be the same. It should be appreciated that a region may be adjacent to another region in one embodiment or the regions may be isolated and, therefore, non-overlapping. When the regions are adjacent, there may be a slight overlap wherein the materials or precise process interactions are not known, however, a portion of the regions, normally at least 50% or more of the area, is uniform and all testing occurs within that region. Further, the potential overlap is only allowed with material of processes that will not adversely affect the result of the tests. Both types of regions are referred to herein as regions or discrete regions.

FIG. 3 illustrates a schematic diagram of a simple TFPV device stack in the substrate configuration consistent with some embodiments of the present invention. The convention will be used wherein light is assumed to be incident upon the top of the material stack in the substrate configuration as illustrated. This generic diagram would be typical of a CIGS TFPV device. A back contact layer, 304, is formed on a substrate, 302. Examples of suitable substrates comprise float glass, low-iron glass, borosilicate glass, flexible glass, specialty glass for high temperature processing, stainless steel, carbon steel, aluminum, copper, titanium, molybdenum, polyimide, plastics, cladded metal foils, etc. Furthermore, the substrates may be processed in many configurations such as single substrate processing, multiple substrate batch processing, inline continuous processing, roll-to-roll processing, etc. As used herein, the phrase “back contact” will be understood to be the primary current conductor layer situated between the substrate and the absorber layer in a substrate configuration TFPV device. An example of a common back contact layer material is Mo for CIGS. The back contact layer may be formed by any number of deposition technologies. Examples of suitable deposition technologies comprise PVD (sputtering), evaporation, chemical vapor deposition (CVD), atomic layer deposition (ALD), plating, etc. The thickness of the back contact layer is typically between about 0.3 um and about 1.0 um. The back contact layer has a number of requirements such as high conductivity, good ohmic contact to the absorber layer, ease of bonding to tabs for external connectivity, ease of scribing or other removal, good thermo-mechanical stability, and chemical resistance during subsequent processing, among others.

Optionally, a diffusion barrier layer (not shown) may be formed between the substrate and the back contact layer. When implemented, the diffusion barrier layer stops the diffusion of impurities from the substrate into the back contact layer, or alternatively, stops the diffusion and reaction of the back contact material into the substrate. Examples of common diffusion barrier layers comprise chromium, vanadium, tungsten, nitrides such as tantalum nitride, tungsten nitride, titanium nitride, silicon nitride, zirconium nitride, hafnium nitride, oxy-nitrides such as tantalum oxy-nitride, tungsten oxy-nitride, titanium oxy-nitride, silicon oxy-nitride, zirconium oxy-nitride, hafnium oxy-nitride, oxides such as aluminum oxide, silicon oxide, carbides such as silicon carbide, binary and/or multinary compounds of tungsten, titanium, molybdenum, chromium, vanadium, tantalum, hafnium, zirconium, and/or niobium with/without the inclusion of nitrogen and/or oxygen. The diffusion barrier layer may be formed from any well known technique such as sputtering, CVD, evaporation, wet methods such as printing or spraying of inks, screen printing, inkjet printing, slot die coating, gravure printing, wet chemical depositions, or from sol-gel methods such as the coating, drying, and firing of polysilazanes.

A p-type absorber layer, 306, of CIGS (or other IB-IIIA-VIA material) is then deposited on top of the back contact layer. The absorber layer may be formed using a variety of techniques such as PVD (sputtering), co-evaporation, in-line evaporation, plating, printing or spraying of inks, screen printing, inkjet printing, slot die coating, gravure printing, wet chemical depositions, CVD, etc. Advantageously, the absorber layer is deficient in Cu. The Cu deficiency may be controlled by managing the deposition conditions. Advantageously, a small amount of Na is contained in the absorber layer. The Na may be added by out-diffusion from the SLG substrate or may be purposely added in the form of Na₂Se or another sodium source, prior, during, or after the deposition of the absorber layer. Typically, the absorber layer undergoes a selenization process after formation to convert the precursor to CIGS into a high-quality CIGS semiconductor film. The selenization process involves the exposure of the absorber layer to a Se-containing gas comprising at least one of H₂Se, Se vapor, or diethylselenide (DESe) at temperatures most typically between about 300 C and 700 C. It should be noted that the precursor to CIGS might already contain a chalcogen source (e.g. Se), either as a separate layer, or incorporated into the bulk of the precursor layer. The precursor film can be a stack of layers, or one layer. The precursor layer can be dense, or porous. The precursor film typically contains Cu, In, and Ga. The precursor layer is most commonly deposited by sputtering from e.g. binary copper-gallium and Indium sputter targets. Nevertheless, plating and printing to deposit the metal precursor film containing Cu, In, and/or Ga are used as well. During the selenization process, a layer of Mo(S)Se₂ (not shown) forms at the back contact/absorber layer interface and forms a fairly good ohmic contact between the two layers. The thickness of the absorber layer is typically between about 1.0 um and about 3.0 um. The performance of the absorber layer is sensitive to materials properties such as crystallinity, grain size, surface roughness, composition, defect concentration, etc. as well as processing parameters such as temperature, deposition rate, thermal treatments, etc.

An n-type buffer layer, 308, is then deposited on top of the absorber layer. Examples of suitable n-type buffer layers comprise CdS, ZnS, In₂S₃, In₂(S,Se)₃, CdZnS, ZnO, Zn(O,S), (Zn,Mg)O, etc. CdS is the material most often used as the n-type buffer layer in CIGS TFPV devices. The buffer layer may be deposited using chemical bath deposition (CBD), chemical surface deposition (CSD), PVD (sputtering), printing, plating, ALD, Ion-Layer-Gas-Reaction (ILGAR), or evaporation. The thickness of the buffer layer is typically between about 30 nm and about 100 nm. The performance of the buffer layer is sensitive to materials properties such as crystallinity, grain size, surface roughness, composition, defect concentration, etc. as well as processing parameters such as temperature, deposition rate, thermal treatments, etc.

Optionally, an intrinsic ZnO (iZnO) layer, 310, is then formed on top of the buffer layer. The iZnO layer is a high resistivity material and forms part of the transparent conductive oxide (TCO) stack that serves as part of the front contact structure. The TCO stack is formed from transparent conductive metal oxide materials and collects charge across the face of the TFPV solar cell and conducts the charge to tabs used to connect the solar cell to external loads. The iZnO layer makes the TFPV solar cell less sensitive to lateral non-uniformities caused by differences in composition or defect concentration in the absorber and/or buffer layers. The iZnO layer is typically between about 0 nm and 150 nm in thickness. The iZnO layer is typically formed using a (reactive) PVD (sputtering) technique or CVD technique, but can be deposited by plating or printing as well. A low resistivity top TCO layer, 312, (examples include Al:ZnO (AZO), InSnO (ITO), InZnO, B:ZnO, Ga:ZnO, F:ZnO, F:SnO₂, etc.) is formed on top of the iZnO layer. The top TCO layer is typically between about 0.25 um and 1.0 um in thickness. The top TCO layer is typically formed using a (reactive) PVD technique or CVD technique. Optionally, the transparent top electrode can be printed or wet-coated from nano-wires, carbon nanotubes, and the like.

FIG. 4 illustrates a schematic diagram of a combinatorial PVD system according to an embodiment described herein. Details of the combinatorial PVD system are described in U.S. patent application Ser. No. 12/027,980 filed on Feb. 7, 2008 and claiming priority to Sep. 5, 2007 and U.S. patent application Ser. No. 12/028,643 filed on Feb. 8, 2008 and claiming priority to Sep. 5, 2007. Substrate, 400, is held on substrate support, 402. Substrate support, 402, has two axes of rotation, 404 and 406. The two axes of rotation are not aligned. This feature allows different regions of the substrate to be accessed for processing in a site isolated manner. The substrate support may be moved in a vertical direction to alter the spacing between the PVD targets and the substrate. The combinatorial PVD system comprises multiple PVD assemblies configured within a PVD chamber (not shown). In FIG. 4, three PVD assemblies are shown, 408 a-408 c. Those skilled in the art will appreciate that any number of PVD assemblies may be used, limited only by the size of the chamber and the size of the PVD assemblies. Typically, four PVD assemblies are contained within the chamber. Advantageously, the multiple PVD assemblies contain different target materials to allow a wide range of material and alloys compositions to be investigated. Additionally, the combinatorial PVD system will typically include the capability for reactive sputtering in reactive gases such as O₂, NH₃, N₂, etc. The PVD assemblies may be moved in a vertical direction to alter the spacing between the PVD targets and the substrate and may be tilted to alter the angle of incidence of the sputtered material arriving at the substrate surface. The combinatorial PVD system further comprises a process kit shield assembly, 410. The process kit shield assembly includes an aperture, 412, used to define isolated regions on the surface. The portion of the process kit shield assembly that includes the aperture may have both rotational and translational capabilities. The combination of the substrate support movement, PVD assembly movement, and process kit shield assembly aperture movement allows multiple regions of the substrate to be processed in a site isolated manner wherein each site can be processed without interference from adjacent regions. Advantageously, the process parameters among the multiple site isolated regions can be varied in a combinatorial manner.

FIG. 5 illustrates a schematic diagram of a substrate that has been processed in a combinatorial manner to form isolated regions on the substrate. Although the substrate in FIG. 5 is illustrated as being a generally square shape, those skilled in the art will understand that the substrate may be any useful shape such as round, rectangular, etc. FIG. 5 illustrates a substrate, 500, with nine site isolated regions, 502 a-502 i, illustrated thereon. The lower portion of FIG. 5 illustrates a top down view while the upper portion of FIG. 5 illustrates a cross-sectional view taken through the three site isolated regions, 502 g-502 i. The shading of the nine site isolated regions illustrates that the process parameters used to process these regions have been varied in a combinatorial manner. The substrate may then be processed through a next step that may be conventional or may also be a combinatorial step as discussed earlier with respect to FIG. 2.

FIG. 6 presents SEM micrographs of CIG films formed using different sequences. Cu—In—Ga precursor films were deposited using PVD (sputtering) on Mo-coated soda lime glass. The PVD chamber housed four PVD sources that allowed for sequential or co-sputtering of different film stacks. In some embodiment, the four PVD sources comprised two In sources, a Cu source, and a Cu₆₀Ga₄₀ source. The films were in the thickness range from about 500 nm to about 600 nm and yielded composition ratios of Cu (Cu/(In+Ga) between about 0.8 and about 1.0 and yielded compositions of Ga (Ga/(Ga+In) between about 0.2 and about 0.4. Two different sequencing of precursor deposition was tested: Mo/In/In/Cu/CuGa and Mo/Cu/CuGa/In/In. The combinatorial system discussed with respect to FIG. 4 allows a range of compositions and deposition sequences to be varied in a combinatorial manner and evaluated on a single substrate as illustrated with respect to FIG. 5. The different compositions and deposition sequences can then be processed using the novel selenization method discussed below.

The Cu—In—Ga precursor films formed using the standard process were selenized in a batch furnace in an atmosphere of about 1 molar % H₂Se in Ar at a temperature of 500 C. The pressure within the furnace was held at between about 300 torr and about 740 torr.

Surface morphology and roughness of the Cu—In—Ga metal precursor was investigated with SEM as illustrated in FIG. 6. The SEM micrographs in FIG. 6 (a-d) represent two deposition sequences and two material compositions. Using the base composition of Cu(In_(1−x)Ga_(x)), FIG. 6-a represents a Mo/In/CuGa sequence where x=0.2; FIG. 6-b represents a Mo/CuGa/In sequence where x=0.2; FIG. 6-c represents a Mo/In/CuGa sequence where x=0.4; and FIG. 6-d represents a Mo/CuGa/In sequence where x=0.4. The layer sequence Mo/In/CuGa (SEM micrographs a and c) had a smoother surface morphology compared to Mo/CuGa/In (SEM micrographs b and d). The Mo/CuGa/In sequence (SEM micrographs b and d) had rough morphology due to In island growth on the CuGa surface. Increasing the Ga content reduced the surface roughness by reducing the In concentration. Photoluminescence (PL) and device results showed the surface roughness had strong effects on the performance of the absorber. CIGS made with the rougher Mo/CuGa/In sequence had lower PL intensity and worse device results compared to the smoother Mo/In/CuGa sequence.

It is desirable to optimize the selenization of the metal precursors by increasing the reaction temperature. At temperatures above the furnace temperature of 550 C, In agglomeration competed against selenization. When In agglomeration was preferred over selenization, In particulates segregated from the metal precursor and formed separate binary phases. The resulting films had spotty and blister-like visual appearance. X-ray diffraction (XRD) spectra on these films showed InSe (004) and (006) peaks besides ternary chalcopyrite. There was no PL intensity on these films and device results were poor. To solve this problem, an intermediate, lower temperature selenization step at between about 350 C and about 450 C was introduced to partially selenize the precursor before complete selenization at higher temperatures. The additional step secured the In in a selenized state to prevent agglomeration. This eliminated the problem of binary phase formation in the final selenization step.

Another problem typically encountered during selenization is the difficulty to control the degree of selenization at higher reaction temperatures. The selenization reaction of CIGS occurs at temperatures above about 350 to about 450 C. In a batch furnace, the ramp rates are generally limited to about 10 C/min by hardware. When the maximum reaction temperature is increased, both the reaction rate and the reaction time are increased, including the period of time for heating up and cooling down. When the furnace temperature was increased to 600 C, delamination at the Mo/CIGS interface occurred due to over-selenization and formation of a thick MoSe₂ layer. In some embodiments of the present invention, a fast gas exchange step is introduced at the high temperature step to replace H₂Se in the furnace with an inert gas such as Ar, N₂, etc. to stop further selenization. This resolves the delamination problem due to over-selenization by limiting the formation of the MoSe₂ layer.

FIG. 7 illustrates a schematic diagram of furnace temperature profiles for the standard 500 C process and the 625 C process described in some embodiments herein. FIG. 7 a) illustrates a schematic diagram of furnace temperature profiles for the standard 500 C process. After the substrates are loaded into the furnace, the temperature is raised slowly from about room temperature to about 200 C while flowing about 1 molar % H₂Se in Ar. After reaching a temperature of about 200 C, the substrates are held at a temperature of about 200 C until the substrates reach thermal equilibrium. The slow ramp and soak at low temperature ensures that the substrate and the deposited Cu—In—Ga metal precursor film do not suffer from thermal shock. In the next step, the temperature is raised to about 500 C and the Cu—In—Ga metal precursor film selenized for a period of time. The flow of the H₂Se is stopped and the temperature is then lowered back to about room temperature.

FIG. 7 b) illustrates a schematic diagram of furnace temperature profiles for the 625 C process described in some embodiments herein. After the substrates are loaded into the furnace, the temperature is raised slowly from about room temperature to about 200 C while flowing about 1 molar % H₂Se in Ar. After reaching a temperature of about 200 C, the substrates are held at a temperature of about 200 C until the substrates reach thermal equilibrium. The slow ramp and soak at low temperature ensures that the substrate and the deposited Cu—In—Ga metal precursor film do not suffer from thermal shock. In the next step, the temperature is raised to between about 350 C and about 450 C and preferably between about 400 C and about 450 C and the Cu—In—Ga metal precursor film is partially selenized for a period of time. As mentioned above, this step secures the In in a selenized state and helps to prevent agglomeration. In the next step, the temperature is raised to between about 550 C and about 650 C and preferably to about 625 C and the Cu—In—Ga metal precursor film selenized for a period of time. The higher temperature is possible due to the earlier reaction of the In with the H₂Se during the initial low temperature partial selenization step. The higher temperature results in increased crystallinity, larger grains, and improved optoelectronic performance. To prevent the over-selenization of the film, a fast gas exchange step is introduced near the beginning of the 625 C step. In this process, the H₂Se flow is stopped and the H₂Se gas within the furnace is quickly removed through a combination of an increased inert gas purge and pumping capacity. The CIGS film can be annealed at about 625 C to influence the Ga distribution throughout the depth of the film.

FIG. 8 presents SEM micrographs of CIGS films formed using different selenization treatments. The SEM micrograph in FIG. 8 a) presents a cross sectional view of a CIGS film selenized using the standard 500 C selenization process. As can be seen, the film comprises multiple small grains that traverse the thickness of the film. The SEM micrograph in FIG. 8 b) presents a cross sectional view of a CIGS film selenized using the 625 C selenization process described in some embodiments of the present invention. As can be seen, the film comprises single, large, columnar grains of between about 0.5 um and about 1.0 um in size that traverse the thickness of the film. The larger grain size can be advantageous since light generated minority carriers in the absorber do not need to cross grain boundaries to reach the junction. This may improve minority carrier life time by reducing grain boundary recombination rate. XRD spectra of these CIGS films exhibited the preferred orientation in (112). The film selenized at about 625 C exhibited a narrower full width at half-max (FWHM) of 0.30 degrees compared to 0.40 degrees for the film selenized at 500 C. The narrowness of the XRD peak is an indication of the quality of the crystallization. The improvements in grain size and crystallinity are benefits of the higher growth temperature of the CIGS film.

Elemental distribution in depth was investigated. CIGS films selenized at 500 C showed the typical Ga accumulation towards the Mo back contact. This is illustrated in FIG. 9 wherein the Ga can be clearly seen to accumulate near the CIGS/Mo interface. For the films selenized at 625 C, the Ga concentration at the surface was increased. This is illustrated in FIG. 10 wherein the Ga can be clearly seen to exhibit a much more consistent profile throughout the film and the concentration of Ga at the surface has been markedly increased relative to the films selenized at 500 C using the standard process sequence. The temperature profile during selenization was adjusted so that there was a shallow Ga gradient increasing towards the Mo back contact. This created a back surface field that could reduce back surface recombination and enhance minority carrier collection.

Spectral resolved room temperature PL was used to measure the band gap and quality of the CIGS absorber layer. Due to the large absorption coefficient of CIGS (about 10⁵/cm) at the excitation wavelength (660 nm), PL probed only the top about 1/10 to about 1/20 surface layer of the film thickness. Therefore, the PL peak energy position was a good indication of the surface band gap of the CIGS absorber layer. FIG. 11 presents photoluminescence data from CIGS films formed using different selenization treatments. FIG. 11 illustrates that the band gap increased from about 0.98 eV to about 1.07 eV comparing films selenized at 500 C and 625 C. This demonstrated the effectiveness of band gap increase by enhancing Ga diffusion using the high temperature selenization process. The intensity of PL is a measure of the radiative recombination rate of the semiconductor. High quality material should have high PL intensity with low non-radiative recombination rates.

The discussion above has described the implementation of some embodiments of the present invention in a batch system. However, the methods may be implemented on other equipment configurations. In some embodiments of the present invention, the methods are implemented on an in-line system configuration. In an in-line system, the substrates are conveyed through multiple chambers or sections on a belt or conveyor, usually comprises of metal or ceramic. The substrates may move through the sequence of chambers in a step-wise manner or a continuous manner. The chambers may operate at atmospheric pressure or may operate at pressures below atmospheric pressure. The substrates may be heated in the various chambers or sections using heating technology such as resistive heating or lamp heating.

In some embodiments of the present invention, substrates are conveyed through a first chamber that raises the temperature of the substrate from about room temperature to about 200 C in the presence of about 1 molar % H₂Se in Ar. After reaching a temperature of about 200 C, the substrates are held at a temperature of about 200 C until the substrates reach thermal equilibrium. The slow ramp and soak at low temperature ensures that the substrate and the deposited Cu—In—Ga metal precursor film do not suffer from thermal shock. In the next chamber, the temperature is raised to between about 350 C and about 450 C and preferably to between about 400 C and about 450 C in the presence of about 1 molar % H₂Se in Ar and the Cu—In—Ga metal precursor film is partially selenized for a period of time. As mentioned above, this step secures the In in a selenized state and helps to prevent agglomeration. In the next chamber, the temperature is raised to between about 550 C and about 650 C and preferably to about 625 C and the Cu—In—Ga metal precursor film selenized for a period of time. The higher temperature is possible due to the earlier reaction of the In with the H₂Se during the initial low temperature partial selenization step. The higher temperature results in increased crystallinity, larger grains, and improved optoelectronic performance. To prevent the over-selenization of the film, this step is executed without the presence of H₂Se in the chamber. The CIGS film can be annealed at between about 550 C and about 650 C to influence the Ga distribution throughout the depth of the film.

In some embodiments of the present invention, the methods are implemented on a rapid thermal processing (RTP) system configuration. In an RTP system, the temperature of the substrates is increased and controlled through the use of lamp heaters while the substrates reside in a process chamber. The chambers may operate at atmospheric pressure or may operate at pressures below atmospheric pressure.

In some embodiments of the present invention, substrates are loaded into a chamber that raises the temperature of the substrate from about room temperature to about 200 C in the presence of about 1 molar % H₂Se in Ar. After reaching a temperature of about 200 C, the substrates are held at a temperature of about 200 C until the substrates reach thermal equilibrium. The slow ramp and soak at low temperature ensures that the substrate and the deposited Cu—In—Ga metal precursor film do not suffer from thermal shock. In the next step, the temperature is raised to between about 350 C and about 450 C and preferably to between about 400 C and about 450 C in the presence of about 1 molar % H₂Se in Ar and the Cu—In—Ga metal precursor film is partially selenized for a period of time. As mentioned above, this step secures the In in a selenized state and helps to prevent agglomeration. In the next step, the temperature is raised to between about 550 C and about 650 C and preferably to about 625 C and the Cu—In—Ga metal precursor film selenized for a period of time. The higher temperature is possible due to the earlier reaction of the In with the H₂Se during the initial low temperature partial selenization step. The higher temperature results in increased crystallinity, larger grains, and improved optoelectronic performance. To prevent the over-selenization of the film, a fast gas exchange step is introduced near the beginning of the high temperature step. In this process, the H₂Se flow is stopped and the H₂Se gas within the chamber is quickly removed through a combination of an increased inert gas purge and pumping capacity. The CIGS film can be annealed at between about 550 C and about 650 C to influence the Ga distribution throughout the depth of the film.

FIG. 12 illustrates a flow chart that summarizes the salient steps of the methods used in some embodiments of the present invention. Typical steps that are well known by those with skill in the art have been omitted for brevity. In step 1200, the Cu—In—Ga metal precursor film is partially selenized at a temperature between about 350 C and about 450 C in a Se-containing atmosphere. The selenization process typically involves the exposure of the absorber layer to a Se-containing gas comprising at least one of H₂Se, Se vapor, or diethylselenide (DESe). In step 1202, the Cu—In—Ga metal precursor film is more fully selenized at a temperature between about 550 C and about 650 C in a Se-containing atmosphere. The selenization process typically involves the exposure of the absorber layer to a Se-containing gas comprising at least one of H₂Se, Se vapor, or diethylselenide (DESe). In step 1204, the Se-containing component of the atmosphere is removed through a rapid gas exchange process. In this step, the Se-containing gas flow is stopped and the Se-containing gas within the furnace is quickly removed through a combination of an increased inert gas purge and pumping capacity. In step 1206, the CIGS film can be annealed at between about 550 C and about 650 C to influence the Ga distribution throughout the depth of the film.

Although the foregoing examples have been described in some detail for purposes of clarity of understanding, the invention is not limited to the details provided. There are many alternative ways of implementing the invention. The disclosed examples are illustrative and not restrictive. 

What is claimed:
 1. A method for selenizing a Cu—In—Ga precursor film at high temperatures comprising: forming the Cu—In—Ga precursor film on a substrate; heating the substrate to a first temperature between about 350 C and about 450 C in an atmosphere comprising a Se-containing gas; heating the substrate to a second temperature between about 550 C and about 650 C in an atmosphere comprising a Se-containing gas; removing the Se-containing gas from the heating atmosphere; and heating the substrate at the second temperature.
 2. The method of claim 1 wherein the Se-containing gas comprises one of H₂Se, Se vapor, or diethylselenide (DESe).
 3. The method of claim 2 wherein the Se-containing gas is H₂Se.
 4. The method of claim 1 wherein the first temperature is between about 400 C and about 450 C.
 5. The method of claim 1 wherein the second temperature is between about 600 C and about 650 C.
 6. The method of claim 5 wherein the second temperature is about 625 C.
 7. The method of claim 1 wherein the Cu concentration in the Cu—In—Ga precursor film is between about 0.8 and 1.0 and is calculated as (Cu/(In+Ga)).
 8. The method of claim 1 wherein the Ga concentration in the Cu—In—Ga precursor film is between about 0.2 and 0.4 and is calculated as (Ga/(Ga+In)).
 9. The method of claim 1 wherein the method is performed in a batch system.
 10. The method of claim 1 wherein the method is performed in an in-line system.
 11. The method of claim 1 wherein the method is performed in an RTP system.
 12. A method for processing a substrate in a combinatorial manner comprising: forming a plurality of Cu—In—Ga precursor films on isolated regions of the substrate wherein the composition of the Cu—In—Ga precursor films is varied in a combinatorial manner; heating the substrate to a first temperature between about 350 C and about 450 C in an atmosphere comprising a Se-containing gas; heating the substrate to a second temperature between about 550 C and about 650 C 450 C in an atmosphere comprising a Se-containing gas; removing the Se-containing gas from the heating atmosphere; and heating the substrate at the second temperature.
 13. The method of claim 12 wherein the Se-containing gas comprises one of H₂Se, Se vapor, or diethylselenide (DESe).
 14. The method of claim 13 wherein the Se-containing gas is H₂Se.
 15. The method of claim 12 wherein the first temperature is between about 400 C and about 450 C.
 16. The method of claim 12 wherein the second temperature is between about 600 C and about 650 C.
 17. The method of claim 16 wherein the second temperature is about 625 C.
 18. The method of claim 12 wherein the Cu concentration in the Cu—In—Ga precursor film is between about 0.8 and 1.0 and is calculated as (Cu/(In+Ga)).
 19. The method of claim 12 wherein the Ga concentration in the Cu—In—Ga precursor film is between about 0.2 and 0.4 and is calculated as (Ga/(Ga+In)). 